Molding shrinkage: 0.1-0.5%
Thickness: 2.0-50.mm
Water absorption (24H):0.1-0.4%
Softening point of thawing degree: 89 C
Thermal deformation temperature: 70 C
Soft PVC
Tube temperature: 140-170 degrees centigrade
Mold temperature: 40-60 degrees centigrade
Drying temperature: 80 centigrade x2h
Ejection pressure: 600-1500kg/cm2
Density: 1.4g/cm3
Molding shrinkage: 0.1-0.5%╓ PP台湾台化B1101」
Thickness: 2.0-50.mm
Water absorption (24H):0.1-0.4%
Softening point of thawing degree: 85 C
Thermal deformation temperature: 55 C
material processing
Polyvinyl chloride plastics are different in different forms, and the processing methods are varied, such as pressing, extrusion, injection, coating and so on. PVC resin particle size, fisheye, bulk density, purity, impurity and porosity on processing have influence; it should paste resin viscosity and gelling properties of paste into account.╓ PP台湾台化B1101」
Polyvinyl chloride is an amorphous polymer with small shrinkage. Before the powder processing, it should be preheated to eliminate water, enhance the plasticizing effect and prevent bubbles. And PVC is very easy to decompose, especially at high temperature, it is more easily decomposed with steel and copper (200 degrees of decomposition temperature). The forming temperature range is small, and the temperature of the material must be strictly controlled. When using a screw type injection machine and a straight through nozzle, the aperture is suitable for preventing the dead angle of the dead angle. Die casting system should be large, gate section should be large, mould should be cooled, mould temperature is 30-60 degrees, and the temperature of material is 160-190.
Under glass transition temperature (Tg, 80 degrees), polyvinyl chloride is a glassy state. At Tg to viscous temperature (Tf, about 160 degrees), it has high elastic rubber and plasticity, and Tf to thermal decomposition temperature (Td) is viscous flow state. The higher the temperature is, the easier the flow is. When the
2月8日报道，印尼钢铁协会发布的数据显示，2017年印尼进口钢铁643万吨，占其年钢铁消耗总量的48%；2015年和2016年，印尼分别进口钢铁685万吨和649万吨，为全球五大钢铁进口国之一。印尼目前年钢铁消费1340万吨，预计到2025年将达2300万吨。印尼钢铁协会普沃诺表示，印尼正常进口量应为总消耗量的30%，但钢铁生产不足，不得不大量进口。为降低进口依赖，印尼工业部加紧钢铁国产化进程，计划在南加里曼丹和中苏拉维西分别建设3个大型钢铁生产厂，总投资额148.9亿美元。




temperature is over Td, PVC decomposes a large amount of hydrogen chloride (HCl), and the material loses chemical stability and physical properties. Therefore, Td is the upper limit temperature of processing. Because of the high intermolecular force, the Tf is very high and even close to the decomposition temperature, so the plasticizer is needed to reduce the Tf. On the other hand, we also need to add stabilizers to improve the Td of PVC to be processed.